Facile synthesis of flower-like 3D ZnO superstructures via solution route
发布时间：2021-03-15点击次数：
- 摘要：A novel flower-like 3D ZnO superstructure with high uniformity was fabricated on a large scale through a facile aqueous solution route at room temperature. The as-prepared ZnO superstructures with a diameter of about 3 mu m are assembled by large amounts of interleaving nanosheets, which have a uniform thickness of about 15 nm and a well-crystalline structure with {10 (1) over bar0} planes as basal facets. The hierarchical microstructures, which were formed via a two-stage nucleation-growth process, highly depend on the concentration of NaOH and trisodium citrate dihydrate. The photoluminescence result indicates that the ZnO superstructures possess a relatively strong UV emission. The photodecomposition of methyl orange indicates that such ZnO superstructures possess excellent photocatalytic activity.