A facile surfactant-free fabrication of single-crystalline truncated Fe3O4 cubes
发布时间：2021-03-15点击次数：
- 关键字：Magnetite; Morphology; Magnetic properties
- 摘要：Single-crystalline truncated Fe3O4 cubes with active basal facets have been successfully fabricated through a facile surfactant-free hydrothermal route. The presented materials were characterized by X-ray diffraction (XRD), field-emission scanning electron microscopy (FE-SEM), energy dispersive spectroscopy (EDS), dynamic light scattering (DLS), selection area electron diffraction (SAED) and magnetic property measurement system (MPMS). The results showed that all products are Fe3O4 with face-center-cubic (FCC) structure. The morphology of Fe3O4 depends on the contents of hydroxide ions, hydrazine hydrate and reaction time. The well-defined truncated Fe3O4 cubes with active basal facets {1 0 0} were fabricated when the pH value, the hydrazine hydrate content and reaction time are 10, 10 mL and 24 h, respectively. The as-prepared Fe3O4 cubes exhibit excellent magnetic properties, which endow the materials with great potential applications in many fields. (C) 2011 Elsevier B.V. All rights reserved.
- 卷号：176
- 期号：9
- 是否译文：否
+
论文成果
个人信息
- 职称：教授
- 学历：博士研究生
- 学位：博士
- 职务：科技处副处长
- 电子邮箱：
其他联系方式
- 移动电话：
- 邮箱：