Preparation and characterization of biocompatible magnetic carbon nanotubes
发布时间：2021-03-15点击次数：
- 关键字：Magnetic; Carbon nanotubes; Biocompatible; Antimicrobial activities
- 摘要：Magnetic carbon nanotubes consisting of multi-wall carbon nanotubes (MWNTs) core and Fe(3)O(4) shell were successfully prepared by in situ thermal decomposition of Fe(acac)(3) or FeCl(3) or Fe(CO)(5) in 2-pyrrolidone containing acid treated MWNTs at 240 degrees C with the protection of nitrogen gas. The samples were characterized by TEM, XRD, SEAD, XPS and superconducting quantum interference device. Also, their biocompatibility was compared with naked carbon nanotubes. The results showed that after coated with Fe(3)O(4) nanoparticles, the obtained magnetic carbon nanotubes show superparamagnetic characteristic at room temperature, and their blocking temperature is about 80 K. The magnetic properties of the nanotubes are relevant to the content of magnetic particles, increasing content of magnetic nanoparticles leads to higher blocking temperature and saturation magnetization. The results of antimicrobial activities to bacterial cells (Escherichia coli) showed that the MWNTs have antimicrobial activity, while the magnetic nanotubes are biocompatible even with a higher concentration than that of MWNTs. (C) 2010 Elsevier B.V. All rights reserved.
- 卷号：257
- 期号：2
- 是否译文：否
+
论文成果
个人信息
- 职称：教授
- 学历：博士研究生
- 学位：博士
- 职务：科技处副处长
- 电子邮箱：
其他联系方式
- 移动电话：
- 邮箱：