Synthesis and field emission properties of silicon carbide nanobelts with a median ridge
- 发布时间：2021-03-15
- 点击次数：
- 摘要：beta-Silicon carbide (beta-SiC) nanobelts with a median ridge have been synthesized for the first time via a template/catalyst-free chemical vapor reaction (CVR) method. The characterization results show that the beta-SiC nanobelts with widths of 1.5 mu m and thickness of about 10-20 nm consist of nanowires with rough surfaces in diameters of 100 nm (median ridge) and two symmetrical lateral flakes with uniform width. A reasonable two-step Vapor-Solid (TSVS) growth mechanism is proposed to explain the formation of the nanobelts on the basis of crystal growth theory. Using the beta-SiC nanobelts as the cathode, the result of field-emission measurements shows that the turn-on field and threshold field of the beta-SiC nanobelts are about 3.2 V mu m(-1) and 5.7 V mu m(-1), respectively. These features make the beta-SiC nanobelts a promising candidate for field emission displays. The beta-SiC nanobelts obtained in this work enrich the family of silicon carbides nanostructures; moreover, the method and growth mechanism could be an effective clue and example for the synthesis of belt-like nanostructures of other materials.
- 卷号：14
- 期号：20
- 是否译文：否
- 上一条：A glassy carbon electrode modified with a composite consisting of reduced graphene oxide, zinc oxide and silver nanoparticles in a chitosan matrix for studying the direct electron transfer of glucose oxidase and for enzymatic sensing of glucose
- 下一条：Direct electrochemistry of cholesterol oxidase immobilized on chitosan-graphene and cholesterol sensing