- Interfacial microstructure evolution and bonding mechanism transformation of CoCrFeMnNi high-entropy alloy joints fabricated by vacuum hot-compression bonding
- 点击次数：
- 关键字：High-entropy alloy; Vacuum hot-compression bonding; Twin-induced interfacial boundary migration; Dynamic recrystallization; Interfacial oxide particle
- 摘要：Vacuum hot-compression bonding (VHCB) is a promising solid-phase bonding technology, but its feasibility and applicability in high entropy alloy (HEA) are still unclear. Herein, the VHCB process of CoCrFeMnNi HEA was investigated, and the interfacial bonding quality was comprehensively evaluated via microstructure characterization and tensile test. Results exhibit that the VHCB enables to obtain the high-quality CoCrFeMnNi HEA joints, and the excellent bonding performance is attributed to the dissolution of interfacial oxide particles (IOPs) (MnCr2O4) and the migration of interfacial grain boundaries (IGBs). The bonding quality results suggest that the sluggish diffusion of the dissolved elements resulted in partial nanoscale IOPs remaining at the original bonding interface, and the mechanical properties of the joints were not compromised when the IOPs were smaller than 35 nm in size and less than 15/100 mm in amount. Crystallographic analysis indicates that the migration behavior of IGBs is closely associated with the evolution of recrystallized grains and twin boundaries in the interfacial region, and the migration mechanism transformed with the rising bonding temperature. Furthermore, a new interfacial bonding mechanism, i.e., twin-induced interfacial boundary migration, was revealed and its beneficial effect on interfacial bonding quality was demonstrated.(c) 2023 The Authors. Published by Elsevier B.V. This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/).
- 卷号：25
- 期号：-
- 是否译文：否
上一条： Enhancement in interfacial bonding quality of CoCrFeMnNi high-entropy alloy vacuum hot-compression bonding via surface shot peening
下一条： Non-synchronous deformation under shot peening post-treatment of SUS304 bar-plate rotary friction weld generates non-monotonic evolution on material and fatigue property