- Non-synchronous deformation under shot peening post-treatment of SUS304 bar-plate rotary friction weld generates non-monotonic evolution on material and fatigue property
- 点击次数：
- 关键字：SUS304 austenite stainless steel; Round bar–plate rotary friction welding; Shot peening; Microstructure; Residual stress; Fatigue life
- 摘要：Shot peening post-treatment was conducted at SUS304 austenite steel bar-plate rotary friction welding joint with fatigue property deterioration from welding flash. along the shotting intensity increasing, non-synchronous deformation of the plate and flash resulted in non-monotonically evolution of local microstructure, residual stresses, and make the fatigue life increased to flash-removed joint level.
- 卷号：
- 期号：29
- 是否译文：否
上一条： Interfacial microstructure evolution and bonding mechanism transformation of CoCrFeMnNi high-entropy alloy joints fabricated by vacuum hot-compression bonding
下一条： Non-monotonic evolution of microstructure and fatigue properties of round bar–plate rotary friction welding joints in 304 austenitic stainless steel