Foaming and Damping Properties of Ethylene Vinyl-Acetate Copolymer/Polylactic Acid Blends

关键字:damping properties; EVM/PLA; foam; foaming structure

摘要:With ethylene vinyl-acetate copolymer (EVM) and polylactic acid (PLA) blends as the matrix, dicumyl peroxide (DCP) as the curing agent and azodicarbonamide (AC) as the foaming agent, EVM/PLA foamed blends were prepared by compression molding. The effects of different amounts of AC, DCP, and silica, as well as varying foaming time, on the cell structure and damping properties of the EVM/PLA-foamed blends were examined by scanning election microscopy (SEM) and dynamic mechanical analysis (DMA). The results showed that the cell size and damping properties varied little with increasing AC content in the compounds; however, the cell size declined slightly as DCP increased and the damping properties rose slightly, exhibiting an optimum set of properties at 5 phr of DCP. The cell size declined dramatically and damping increased significantly as the foaming time was increased. Moreover, both suddenly increased after 5 min foaming. It was found that the damping properties of the foamed materials increased with decreasing cell size and increasing number of cells. The cell size also decreased and damping properties increased as the silica content was increased. The silica interacted more strongly with EVM than with PLA.

卷号:54

期号:2