An Al-12Si/ZnS powder inoculant for eutectic silicon in Al-12Si alloy

关键字:AL-SI ALLOYSCHEMICAL BATH DEPOSITIONMECHANICAL-PROPERTIES

摘要:To obtain high-performance Al-Si-based cast alloys,refinement and modification of Si phases are required.An Al-12Si/ZnS powder inoculant was designed and fabricated using a chemical bath deposition method.The efficiency of the inoculant for modifying the eutectic Si phase in as-cast Al-12Si alloy was studied.Results show that Al-12Si/ZnS powder can significantly refine the eutectic Si in Al-Si cast alloys.The best refinement effect for eutectic Si is achieved with 17.5wt.% Al-12Si/ZnS powder.Coarse long needle-shaped eutectic Si with a length of 18 μm was modified into approximately spherical shape with a diameter of 6.53 μm,which is evenly distributed throughout the alloy.The E2EM model calculation indicates that the inter-plane misfit (F_p) and inter-atomic spacing misfit (F_r) between ZnS and Si are all less than 0.5%,which confirms that ZnS is a potential nucleation site for Si phase.The hardness,tensile strength,and elongation of Al-12Si alloys modified with 17.5% Al-12Si/ZnS powder increase 6.30%,16.18% and 55.45%,respectively,compared to the unmodified Al-12Si alloy.The fracture behavior of the alloy with 17.5wt.% Al-12Si/ZnS powder is dominated by transgranular fracture supplemented by intergranular fracture.

卷号:v.19

期号:02

是否译文:

崂山校区 - 山东省青岛市松岭路99号   
四方校区 - 山东省青岛市郑州路53号   
中德国际合作区(中德校区) - 山东省青岛市西海岸新区团结路3698号
高密校区 - 山东省高密市杏坛西街1号   
济南校区 - 山东省济南市文化东路80号©2015 青岛科技大学    
管理员邮箱:master@qust.edu.cn