Fabrication and characterization of morphology-tuned single-crystal monodisperse Fe<inf>3</inf>O<inf>4</inf>nanocrystals
发布时间：2021-03-15点击次数：
- 关键字：Dispersions;Characterization - Fabrication - Fourier transform infrared spectroscopy - Iron compounds - Magnetic properties - Magnetism - Morphology - Nanocrystals - Single crystals - Transmission electron microscopy - X ray diffraction;Different sizes - Dipolar interaction - Fabrication and characterizations - Face centered cubic structure - High temperature - Magnetic property measurement systems - Mineral processing - Synthesized materials
- 摘要：Monodisperse Fe<inf>3</inf>O<inf>4</inf>nanocrystals with different size and morphology have been successfully fabricated by a facile high temperature reflow method. The presented materials were characterized by X-ray diffraction (XRD), fourier transform infrared (FTIR) spectroscopy, transmission electron microscope (TEM), selection area electron diffraction (SAED) and magnetic property measurement system (MPMS). The results showed that the as-prepared materials have face-centered cubic structures. Oleic acid plays a key role in the dispersion of Fe<inf>3</inf>O<inf>4</inf>nanocrystals. The cubic and octahedral nanocrystals are enclosed by {1 0 0} and {1 1 1} lattice planes. The MPMS measurements show that magnetic properties are closely related to the sizes of the materials, and there is a stronger dipolar interaction between Fe<inf>3</inf>O<inf>4</inf>nanocrystals with larger sizes. The controllable magnetic property and good dispersion endow the as-synthesized materials with great potential applications in magnetic fluid fields including sealing, medical equipment, mineral processing and other aspects.<br/> © 2018 Elsevier B.V.
- 卷号：439
- 是否译文：否
+
论文成果
个人信息
- 职称：教授
- 学历：博士研究生
- 学位：博士
- 职务：科技处副处长
- 电子邮箱：
其他联系方式
- 移动电话：
- 邮箱：