Photo-Thermal Conversion of Copper Sulfide Hollow Structures with Different Shape and Thickness

关键字:Photothermal Conversion; Hollow Structures; Copper Sulfide; Sacrificial Templates

摘要:In the current paper, we report the synthesis of spherical and cubic copper sulfide hollow structures, as well as the influence of shape and thickness on the photo-thermal conversion of the as-synthesized products. Copper sulfide hollow structures of different thickness were synthesized base on a sacrificial template strategy using spherical and cubic Cu2O precursors as templates. Optical absorption of the as-synthesized products was investigated with UV-Vis spectrometer. Photo-thermal conversion property was studied with a lab-made evaluation system equipped with an AUT-FSL semiconductor/solid state laser. The results indicate that the as-prepared products exhibited significant absorption in visible light regions. Under the irradiation of laser beam with a wavelength at 635 nm and a power of 0.015 W, the temperature elevations of the aqueous suspensions containing 0.24% mass fraction of spherical and cubic copper sulfide hollow structures were measured to be 5 degrees C and 6 degrees C within 60 seconds, respectively. On the contrast, water showed little temperature elevation under the same conditions.

卷号:15

期号:4

是否译文:

崂山校区 - 山东省青岛市松岭路99号   
四方校区 - 山东省青岛市郑州路53号   
中德国际合作区(中德校区) - 山东省青岛市西海岸新区团结路3698号
高密校区 - 山东省高密市杏坛西街1号   
济南校区 - 山东省济南市文化东路80号©2015 青岛科技大学    
管理员邮箱:master@qust.edu.cn