The remarkable morphology regulatory effect of NH4+ ions on TiO2 nanorod arrays and their application in dye-sensitized solar cells
- 发布时间：2023-10-19
- 点击次数：
- 关键字：NITROGEN-DOPED TIO2; EFFICIENCY; STATE; PERFORMANCE; NANOTUBES; NANOPARTICLES; 10-PERCENT; SCATTERING; CONVERSION; IMPEDANCE
- 摘要：Nitrogen doping is often used to expand the response range of wide-bandgap semiconductors to improve their photoelectrical properties. Unique morphology regulatory effect of NH4+ ions on one-dimensional TiO2 nanorod arrays (TNAs) is proved in this research for the first time, but nitrogen-doping effect is hardly detected. Once NH4Cl is added, the growth of TNAs is greatly promoted especially in radial direction, but little amount of nitrogen from NH4+ ions can enter the modified TNAs (N-TNAs). Furthermore, the bandgap energy of N-TNAs is almost unchanged compared with TNAs, meaning that trace nitrogen doping does not affect response ability to irradiation. When fabricated into dye-sensitized solar cells (DSSCs) with N-TNAs, the optimal photoelectrical conversion efficiency (3.16%) is nearly twice that with TNAs (1.62%). It is worth noting that the increased efficiency mainly results from the photoinduced current but not voltage. Second, the change of conversion efficiency is related to nanorod length. In summary, the improvement of photoelectrical property is caused by the directional growth of nanorods, which results from the addition of NH4+ ions as an effective structure regulatory agent.
- 卷号：125
- 期号：4
- 是否译文：否