关键字：POLYMER NETWORKS; NANOPARTICLES; BEHAVIOR; PROGRESS
摘要：In this work, polynorbornene (PNB) (plasticized by 50 phr microcrystalline wax) with excellent thermo-triggered shape memory properties was used as the matrix material, in which synthetic polydopamine (PDA) nanospheres were hybrided. Consequently, PNB/PDA composites presented ultrafast near-infrared (NIR) responsive shape memory performance due to PDA's light-to-heat conversion ability. The results showed that PNB/PDA composites hybrided with 1 wt% PDA reached 74 degrees C within 50 s under the irradiation of NIR (808 nm wavelength). NIR-triggered shape memory performance of the PNB/PDA composites increased with the rise of NIR output power. When light power was 2.5w/cm(2), the sample can completely recover its original shape within 20 s. Therefore, PDA-hybrided PNB composites not only have good thermal-responsive shape memory performance, but also have excellent one triggered by NIR, which broaden PNB's responsive ways for shape memory.
卷号：206
期号：
是否译文：否