摘要：The damping properties of ethylene vinyl-acetate copolymer (EVM)/ethylene-propylene-diene monomer (EPDM) and EVM/nitrile butadiene rubber (NBR) blends, with di(tert-butylperoxyisopropyl)benzene (BIBP) as the curing agent, were investigated by dynamic mechanic analyzer (DMA). The effects of PVC, N-cyclohexyl-2-benzothiazole (CZ), and dicumyl peroxide (DCP) on the damping properties were studies. The results show that in EVM/EPDM/PVC blends, PVC and EVM700 are compatible with one tanδ peak, which improves the damping properties of EVM at higher temperature. In EVM/NBR blends, PVC and EVM/NBR blends are partially compatible with two combined tanδ peaks, which widens the effective damping temperature range to 62.4°C. 1.4 phr DCP enlargs the tanδ peak of EVM/NBR with the effective damping temperature range up to 64.9°C. Small amount of CZ can enlarge the tanδ peak of EVM/NBR. 5 phr Zn(AA)2 can also widen the tanδ peak of EVM/NBR.
卷号：27
期号：5
是否译文：否