The m-SiCNW/FKM nanocomposites: fabrication, characterization and properties

  • 发布时间:2023-10-20
  • 点击次数:

  • 关键字:
  • 摘要:Nanocomposites consisting of the fluoroelastomer (FKM) matrix and modified SiC nanowires (m-SiCNWs) as strengthening phase (coded as m-SiCNW/FKM nanocomposites) have been prepared for the first time on an open two-roll mill. SiCNWs were modified by simple chemical treatment using fluoroalkylsilane (AC-FAS, CF3(CF2)(7)CH2CH2Si(OC2H5)(3)) as modifier. Fourier transform infrared spectroscopy (FTIR) indicated that AC-FAS was successfully grafted to the surface of the SiCNWs. The water contact angle test confirmed that the surface of m-SiCNWs was hydrophobic. Compared with FKM, the tensile strength, stress at 100% strain, tear strength and thermal conductivity at 100 degrees C of the nanocomposites with 14 phr m-SiCNWs were improved by 15.3%, 102.0%, 17.6% and 56.9%, respectively. The tensile fracture surface morphology of m-SiCNW/FKM nanocomposites shows that m-SiCNWs were uniformly dispersed, and the interfacial adhesion between m-SiCNWs and FKM matrix was strong. Dynamic mechanical analysis shows that the storage modulus (E') of the m-SiCNW/FKM nanocomposites was improved, and the T-g shifted to a higher temperature by increasing the m-SiCNW content, indicating the greater reinforcing effect of m-SiCNWs. Payne effect, as an important characteristic of rubber materials, was also investigated. The preparation of m-SiCNW/FKM nanocomposites provides a favorable exploration for the application of one-dimensional (1D) nanofiller in polymer composites.
  • 卷号:6
  • 期号:42
  • 是否译文:

崂山校区 - 山东省青岛市松岭路99号   
四方校区 - 山东省青岛市郑州路53号   
中德国际合作区(中德校区) - 山东省青岛市西海岸新区团结路3698号
高密校区 - 山东省高密市杏坛西街1号   
济南校区 - 山东省济南市文化东路80号©2015 青岛科技大学    
管理员邮箱:master@qust.edu.cn