Study on the structure, morphology and properties of Fe-doped Cu3N films

  • 发布时间:2023-10-19
  • 点击次数:

  • 关键字:copper nitride film; Fe doped; thermal stability; energy gap
  • 摘要:Fe-doped Cu3N films were prepared by cylindrical magnetron sputtering equipment at room temperature. The doping of Fe with the proper concentration results in a change in the preferred growth orientation from the Cu-rich plane (1 1 1) to the N-rich plane (1 0 0), which relates to the evolution of the surface grain shape from pyramid to sphere. Excessive doping of Fe is not favourable for the crystallization of Cu3N films. The cross-sections of the doped films with preferred growth orientations of [ 1 0 0] exhibit regular columnar grains. The variation between the lattice constant and the XPS results reveals that Fe probably replaces the position of Cu atoms in the lattice or is segregated in the grain boundaries. Weaker bonding of Cu-N results in a reduction of thermal stability for Fe-doped Cu3N films. And the incorporation of Fe can effectively modify the energy gap. According to the variations in the mean grain size, the peak of N1s and the energy gap, it is inferred that a doping limitation exists around 2.0 at%.
  • 卷号:47
  • 期号:18
  • 是否译文:

崂山校区 - 山东省青岛市松岭路99号   
四方校区 - 山东省青岛市郑州路53号   
中德国际合作区(中德校区) - 山东省青岛市西海岸新区团结路3698号
高密校区 - 山东省高密市杏坛西街1号   
济南校区 - 山东省济南市文化东路80号©2015 青岛科技大学    
管理员邮箱:master@qust.edu.cn