Construction of a robust solid electrolyte interphase on Ge anode to achieve a superior long-term cycle life of lithium-ion battery
- 发布时间：2023-10-19
- 点击次数：
- 关键字：TOTAL-ENERGY CALCULATIONS; IN-SITU CONSTRUCTION; PERFORMANCE; LIQUID
- 摘要：Alloy-based materials are suffering a huge volume expansion/shrink during the repeated lithium-ion in-tercalation/deintercalation process, so they always display an unsatisfied electrochemical performance, especially for the cycle life. In this work, we design a localized highly concentrated electrolyte (LHCE) for Ge anode, by dissolving LiFSI in DME/TTE (3:7 by volume). Raman spectra illustrate that most FSI- anions in LHCE coordinate with Li+ ions, producing the solvated structure in form of AGGs or CIPs. XPS spectra prove that the solid electrolyte interphase (SEI) is rich in inorganic phase, such as Li2CO3, Li3N, LiF and Li2O. So the SEI is more stable and thinner, and it can keep the integrity of Ge particles and avoid their crushing during a long-term cycle. Although a serious capacity decrease at around the 30th cycle is found in esters electro-lytes, the similar phenomenon is never seen in LHCE. The PM-550 @Ge in LHCE remains a reversible ca-pacity of 1040 mAh g-1 after 300 cycles at 0.5 A g-1, and the capacity retention ratio is as high as 84%. Even after a long cycling of 500 cycles, the PM-550 @Ge delivers a high reversible capacity of 951 mAh g-1 at 1.0 A g-1. (c) 2023 Elsevier B.V. All rights reserved.
- 卷号：954
- 期号：
- 是否译文：否
- 上一条：ZIF-8-templated synthesis of core-shell structured IPOP@MOF hybrid-derived nitrogen-doped porous carbon for efficient oxygen reduction electrocatalysis and supercapacitor
- 下一条：Chromium doping and in-grown heterointerface construction for modifying Ni3FeN toward bifunctional electrocatalyst toward alkaline water splitting