New blue-emitting Ca<inf>2(1 − x)</inf>B<inf>2</inf>P<inf>2</inf>O<inf>10</inf>:2xEu<sup>2+</sup>(0.005 ≤ x ≤ 0.030) phosphors: Synthesis and photoluminescence properties
- 发布时间：2021-03-15
- 点击次数：
- 关键字：Light emission;Calcium - Emission spectroscopy - Luminescence - Phosphates - Phosphors - Photoluminescence - Quenching - Scanning electron microscopy - Solid state reactions - X ray diffraction;Blue phosphors - Blue-emitting - Concentration quenching - Excitation and emission spectra - Luminescence properties - Optimal concentration - Photoluminescence properties - Solid state reaction method
- 摘要：A series of new blue-emitting Ca<inf>2(1 − x)</inf>B<inf>2</inf>P<inf>2</inf>O<inf>10</inf>:2xEu<sup>2+</sup>(x = 0.005, 0.010, 0.015, 0.020, 0.025, 0.030 mol%) phosphors were synthesized by the solid state reaction method. The X-ray diffraction (XRD) and scanning electron microscope (SEM) were utilized to characterize the prepared samples. The luminescence properties of the phosphor were studied by excitation and emission spectra. The optimal concentration of Eu<sup>2+</sup>ions in Ca<inf>2</inf>B<inf>2</inf>P<inf>2</inf>O<inf>10</inf>was determined to be x = 0.010 mol%, and the concentration quenching mechanism was studied in detail. These results suggest that Ca<inf>2</inf>B<inf>2</inf>P<inf>2</inf>O<inf>10</inf>:Eu<sup>2+</sup>is a potential blue phosphor for application in WLEDs. © 2016 Elsevier GmbH
- 卷号：127
- 期号：20
- 是否译文：否
- 上一条：Vertically cross-linked and porous CoNi<inf>2</inf>S<inf>4</inf>nanosheets-decorated SiC nanowires with exceptional capacitive performance as a free-standing electrode for asymmetric supercapacitors
- 下一条：Mechanically exfoliated g-C<inf>3</inf>N<inf>4</inf>thin nanosheets by ball milling as high performance photocatalysts