关键字：Nanostructures; Vapor deposition; Catalytic properties
摘要：Silica-coated copper nanoparticles were synthesized by coating copper nanoparticles with a silica shell through microemulsion. The copper nanoparticles are 30-40 nm in diameter and the silica coating is 10 nm in thickness. After coating, copper nanoparticles were encapsulated in a silica matrix. These particles were used as a catalyst for the growth of carbon nanofibers in a tubular furnace. It is found that carbon nanofibers are mirror-symmetric growth and 100 nm in diameter. During growth, the copper nanoparticles moved out of the silica. As the experiment progressed, the interplanar spacing of copper (2 2 0) increased from 0.1288 nm to 0.1306 nm indicating that (2 2 0) plane exhibited high catalytic activity. The out-of-sync growth of different faces provides new evidence for the research of growth mode in carbon nanofibers. (C) 2011 Elsevier Ltd. All rights reserved.