关键字：Strontium compounds;Cables - Depolarization - Electric fields - Electric insulation - Electric space charge - HVDC power transmission - Iron compounds
摘要：For high voltage direct current (HVDC) cable, a semi-conductive layer lies between the conductor and the insulation layer; as the charge migrates the path from the conductor to the insulation material, it will affect space charge injection. In this work, the research idea of changing the injection path of moving charges within semi-conductive layer by magnetic particles was proposed. Semi-conductive composites with different SrFe<inf>12</inf>O<inf>19</inf> contents of 1 wt.%, 5 wt.%, 10 wt.%, 20 wt.%, and 30 wt.% were prepared, and the amount of injected charges in the insulation sample was characterized by space charge distribution, polarization current, and thermally-stimulated depolarization current. The experimental results show that a small amount of SrFe12O19 can significantly reduce charge injection in the insulation sample, owing to the deflection of the charge migration path, and only part of the electrons can enter the insulation sample. When the content is 5 wt.%, the insulation sample has the smallest charge amount, 0.89 &times; 10^-7 C, decreasing by 37%, and the steady-state current is 6.01 &times; 10^-10 A, decreasing by 22%. When SrFe<inf>12</inf>O<inf>19</inf> content exceeds 10 wt.%, the charge suppression effect is not obvious and even leads to the increase of charge amount in the insulation sample, owing to the secondary injection of charges. Most moving charges will deflect towards the horizontal direction and cannot direct access to the insulation sample, resulting in a large number of charges accumulation in the semi-conductive layer. These charges will seriously enhance the interface electric field near the insulation sample, leading to the secondary injection of charges, which are easier to inject into the insulation sample.<br/> &copy; 2019 by the authors.
卷号：11
期号：8
是否译文：否