关键字：MAGNETIC-PROPERTIES; ELECTRODE MATERIAL; KOH ACTIVATION; BIOMASS; CAPACITANCE; NITROGEN; NANOSHEETS; FRAMEWORK; TEMPLATE
摘要：In this work, a strategy consisting of a two-step carbonization and high temperature activation is developed to derive N, S and O co-doped carbon with three-dimensional pores from soybean roots. An optimized porous carbon activated at 700 C (HSRC-700) displays an ultra-high specific surface area of 3107 m(2) g(-1) with rational 3-dimensional pores, contributing to a high capacitance of 486.8 F g(-1) at 0.5 A g(-1), which maintains 230 F g(-1) even at 100 A g(-1). Also, a stable life over 18,400 cycles at 20 A g(-1) with a retention of 92.5% is delivered. Meanwhile, the energy density of a coin-type symmetric supercapacitor with HSRC-700 in 1 M LiPF6 is as high as 59.4 W h kg(-1) at 1500 W kg(-1), and the value remains 33.3 W h kg(-1) at 30,000 W kg( 1). The findings above indicate that green and eco-friendly soybean root-derived porous carbon exhibits great potential in supercapacitors.