青岛科技大学主页平台管理系统周震芳--中文主页-- Epitaxial Electrocrystallization of Magnesium via Synergy of Magnesiophilic Interface, Lattice Matching, and Electrostatic Confinement

化学镀Cu-Co-P非晶合金及其催化性能表征: 点击次数：; 关键字：CARBON CLOTH; NICKEL-HYDROXIDE; GROWTH; PERFORMANCE; NANOSHEETS; BATTERIES; ELECTRODEPOSITION; SPECTROSCOPY; EVOLUTION; CATHODES; 摘要：Rechargeable magnesium batteries are particularly advantageous for renewable energy storage systems. However, the inhomogeneous Mg electrodeposits greatly shorten their cycle life under practical conditions. Herein, the epitaxial electrocrystallization of Mg on a three-dimensional magnesiophilic host is implemented via the synergy of a magnesiophilic interface, lattice matching, and electrostatic confinement effects. The vertically aligned nickel hydroxide nanosheet arrays grown on carbon cloth (abbreviated as "Ni(OH)2@CC") have been delicately designed, which satisfy the essential prerequisite of a low lattice geometrical misfit with Mg (about 2.8%) to realize epitaxial electrocrystallization. Simultaneously, the ionic crystal nature of Ni(OH)2 displays a periodic and hillock-like electrostatic potential field over its exposed facets, which can precisely capture and confine the reduced Mg0 species onto the local electron-enriched sites at the atomic level. The Ni(OH)2@CC substrate undergoes sequential Mg-ion intercalation, underpotential deposition, and electrocrystallization processes, during which the uniform, lamellar Mg electrodeposits with a locked crystallographic orientation are formed. Under practical conditions (10 mA cm-2 and 10 mAh cm-2), the Ni(OH)2@ CC substrate exhibits stable Mg stripping/plating cycle performances over 600 h, 2 orders of magnitude longer than those of the pristine copper foil and carbon cloth substrates.; 卷号：16; 期号：6; 是否译文：否

上一条： Ni-Co-B修饰纳米碳纤维的磁性能与微波吸收性能