Nickel-doped pyrrhotite iron sulfide nanosheets as a highly efficient electrocatalyst for water splitting

  • 发布时间:2023-10-19
  • 点击次数:

  • 关键字:OXYGEN EVOLUTION; ULTRATHIN NANOSHEETS; NI FOAM; FE; CATALYSTS; OXIDATION; NANOCRYSTALS; GENERATION; MECHANISM; ELECTRODE
  • 摘要:The synthesis of highly active, stable and cost-effective electrocatalysts for overall water splitting is critical but challenging. Herein, we synthesized nickel-doped pyrrhotite iron sulfide (Fe0.95-xNixS1.05) nanosheetsviaa one-pot synthetic route. When tested for oxygen evolution reaction (OER) performance in alkaline solutions, the as-prepared Fe(0.8)Ni(0.15)S(1.05)catalyst exhibited superior electrocatalytic performance to commercial IrO(2)with a current density of 10 mA cm(-2)at an overpotential of 228 mV, and a Tafel slope of 53 mV dec(-1). The hydrogen evolution reaction (HER) activity was achieved on Fe(0.8)Ni(0.15)S(1.05)with a Tafel slope of 103 mV per decade, and a current density of 10 mA cm(-2)at an overpotential of 263 mV. With nickel doping, the as-prepared pyrrhotite iron sulfide nanosheets can expose more active sites, and hence act as a highly efficient catalyst for overall water splitting.
  • 卷号:8
  • 期号:39
  • 是否译文:

崂山校区 - 山东省青岛市松岭路99号   
四方校区 - 山东省青岛市郑州路53号   
中德国际合作区(中德校区) - 山东省青岛市西海岸新区团结路3698号
高密校区 - 山东省高密市杏坛西街1号   
济南校区 - 山东省济南市文化东路80号©2015 青岛科技大学    
管理员邮箱:master@qust.edu.cn