Interfacial Engineering and a Low-Crystalline Strategy for HighPerformance Supercapacitor Negative Electrodes: Fe2P2O7 Nanoplates Anchored on N/P Co-doped Graphene Nanotubes

  • 发布时间:2023-10-19
  • 点击次数:

  • 关键字:OXYGEN REDUCTION; CONTROLLABLE SYNTHESIS; RATE PERFORMANCE; ANODE MATERIALS; ENERGY-STORAGE; CATALYSTS; NANOPARTICLES; COMPOSITES; STABILITY; EVOLUTION
  • 摘要:Developing novel hybrid negative electrode materials with high specific capacity, rate capacitance, and long-term cycle stability is a key factor for pushing large-scale application of supercapacitors. However, construction of robust interfaces and low-crystalline active materials plays a crucial role in realizing the target. In this paper, a one-step phosphorization approach was employed to make low-crystalline Fe2P2O7 nanoplates closely bonded to N/P-co-doped graphene nanotubes (N/P-GNTs@b-Fe2P2O7) through interfacial chemical bonding. The N and P heteroatoms as substitutions for C in GNT skeletons can introduce rich electronic centers, which induces Fe2P2O7 to fix the surface of N/P-GNTs through Fe-N and Fe-P bonds as confirmed by the characterizations. Moreover, the lowcrystalline active materials own a disordered internal structure and numerous defects, which not only endows with excellent conductivity but also provides many active sites for redox reactions. Benefiting from the synergistic effects, the prepared N/P-GNTs@b-Fe2P2O7 can not only deliver a high capacity of 257 mA h g(-1) (927 F g(-1)) at 1 A g(-1) but also present an excellent rate capability of 184 mA h g(-1) (665 F g(-1)) at 50 A g(-1) and outstanding cycle stability (similar to 90.6% capacity retention over 40,000 cycles). Furthermore, an asymmetric supercapacitor was assembled using the obtained N/P-GNTs@b-Fe2P2O7 as electrode materials, which can present the energy density as high as 83.3 W h kg(-1) at 791 W kg(-1) and long-term durability. Therefore, this strategy not only offers an effective pathway for achieving high-performance negative electrode materials but also lays a foundation for further industrialization.
  • 卷号:14
  • 期号:2
  • 是否译文:

崂山校区 - 山东省青岛市松岭路99号   
四方校区 - 山东省青岛市郑州路53号   
中德国际合作区(中德校区) - 山东省青岛市西海岸新区团结路3698号
高密校区 - 山东省高密市杏坛西街1号   
济南校区 - 山东省济南市文化东路80号©2015 青岛科技大学    
管理员邮箱:master@qust.edu.cn