Preparation of NF/rGO/Co3O4/NiO Electrode and Its Application in Supercapacitor

发布时间:2021-03-15  点击次数:

关键字:Supercapacitor; Electrochemical deposition; Reduced graphene oxide(rGO); Metallic oxide

摘要:The electrochemical deposition method was used to prepare NF/rGO/Co3O4 and NF/rGO/Co3O4/ NiO electrodes(NF = nickel foam; rGO = reduced graphene oxide). Here, with NF as a current collector, rGO, Co3O4 and NiO were grown on NF directly without any binder under specific conditions including optimized potential, time and concentration. NF/rGO/Co3O4 and NF/rGO/Co3O4 /NiO electrodes were used as the electrode of supercapacitor, and three. electrode system was employed in cyclic voltammetry, galvanostatic charge. discharge and electrochemical impe. dance spectroscopy characterization of the electrodes. The results showed that the capacitance of NF/rGO/Co3O4 /NiO electrode was 1188.. 6 F/g at 2 A/g; its rate capability was 75.. 7% when the current density varied from 2 A/g to 12 A/g; and its cycling stability was 80.. 5% after 2000 times. Compared with NF/rGO/Co3O4, the supercapacitor performance of NF/rGO/Co3O4 /NiO electrode improved a lot, which can be attributed to the synergistic effect of Co3O4 and NiO. What's more, rGO could enhance the electroconductivity of electrodes to a large extent.

卷号:38

期号:11

是否译文:

崂山校区 - 山东省青岛市松岭路99号   
四方校区 - 山东省青岛市郑州路53号   
中德国际合作区(中德校区) - 山东省青岛市西海岸新区团结路3698号
高密校区 - 山东省高密市杏坛西街1号   
济南校区 - 山东省济南市文化东路80号©2015 青岛科技大学    
管理员邮箱:master@qust.edu.cn

访问量: | 最后更新时间:-- | 开通时间:-- |手机版