关键字：SILICON-CARBIDE NANOWIRES; MORPHOLOGY

摘要：Lanthanum (La)-doped SiC nanowires (NMs) were synthesized via a carbon thermal reduction process using different graphite powders, while milled Si-SiO2 mixed powders were employed as the silicon source. The identification of the products as beta-SiC were supported by Select-area electron diffraction (SAED) and X-ray diffraction (XRD) analysis. The field emission results demonstrated that the turn-on field reached a minimum value of approximately 2.3 V/mu m when the graphite content ranged from 2.5 g-3 g. The product exhibited higher density at this stage, accompanied by an increase in nanowire diameter and a tendency toward straightness. The energy spectrum analysis revealed a significant increase in the lanthanum content within the nanowires, with the atomic percentage rising from 0.05 to 0.26-0.27. The synergistic effect of morphology and La improved the field emission performance of the product. The findings may offer valuable insights for enhancing the field emission performance of one-dimensional nanomaterials.

卷号：648

期号：

是否译文：否