Oxidation with potassium ferrate for the one-pot preparation of carboxylated cellulose II nanocrystals

关键字:THERMAL-STABILITY; IONIC LIQUID; EMULSIONS; STABILIZATION; PRETREATMENT

摘要:Cellulose II nanocrystals (CNC II) possess a higher thermal stability and improved emulsifying capability than cellulose I nanocrystals (CNC I) owing to the higher density of their hydrogen bonds and more larger surface areas. Therefore, CNC II exhibit substantial advantages for value-added nanocomposite materials. Current CNC II preparation methods are mainly based on a two-pot reaction involving acid hydrolysis and crystal transformation. In this study, considering the oxidative nature of potassium ferrate (K2FeO4) in an alkaline environment containing a small amount of sodium hypochlorite (NaClO), a one-step and efficient approach was developed for the preparation of carboxyl-bearing CNC II from cotton pulp, affording a maximum CNC II yield of 45.14 %. Atomic force microscopy analysis revealed that the prepared CNCs exhibited a "rod-like" shape with a width of similar to 7 nm and a length of similar to 269 nm. The resulting CNC II also exhibited excellent thermal stability (T-onset = 311.4 C-degrees). Furthermore, high-internal-phase Pickering emulsions (HIPPEs) stabilized by CNC II were prepared to stabilize liquid paraffin in the absence of surfactant. The results revealed that CNC II could be used as an effective emulsifier to fabricate the stable and gel-like HIPPEs, and are promising for the preparation of high value-added nanocomposite materials.

卷号:329

期号:

是否译文:

崂山校区 - 山东省青岛市松岭路99号   
四方校区 - 山东省青岛市郑州路53号   
中德国际合作区(中德校区) - 山东省青岛市西海岸新区团结路3698号
高密校区 - 山东省高密市杏坛西街1号   
济南校区 - 山东省济南市文化东路80号©2015 青岛科技大学    
管理员邮箱:master@qust.edu.cn