Polymorphism and Structural Transition around 54 degrees C in Regioregular Poly(3-hexylthiophene) with High Crystallinity As Revealed by Infrared Spectroscopy

摘要:Poly(3-hexyllthiophene) (P3HT) with high crystallinity was prepared by controlling the solvent evaporation rate together with the aid of chloroform vapor annealing. According to the infrared spectroscopy combined with the thermal analysis and the X-ray diffraction (XRD) data, a new crystal modification named as form I' was identified for P3HT sample crystallized under extremely slow evaporation rate at low temperature (13 degrees C). Such crystal modification has shorter interlayer distance than that of the more common but more disordered form I of P3HT. Moreover, it demonstrates a distinct endothermic peak around 54 degrees C and a characteristic IR band at 823 cm(-1), which have never been reported for P3HT in the literature. The origin of the structural transition around 54 degrees C is investigated in detail by temperature-dependent infrared spectroscopy combined with the in situ synchrotron WAXD measurement. It is found that, during the heating process of P3HT form crystal, there is the form I'-to-form I phase transition from 30 to 60 degrees C, which belongs to the solid-to-solid phase transition.

卷号:44

期号:23

是否译文:

崂山校区 - 山东省青岛市松岭路99号   
四方校区 - 山东省青岛市郑州路53号   
中德国际合作区(中德校区) - 山东省青岛市西海岸新区团结路3698号
高密校区 - 山东省高密市杏坛西街1号   
济南校区 - 山东省济南市文化东路80号©2015 青岛科技大学    
管理员邮箱:master@qust.edu.cn