Effects of microstructures of liquid polyisoprene on the properties of styrene-butadiene rubber/butadiene rubber compounds
点击次数:
关键字:THERMAL AGING BEHAVIOR; MECHANICAL-PROPERTIES; NATURAL-RUBBER; SILICA; POLYMERS; FILLER
摘要:Recently, there has been an increasing interest in liquid rubbers (LRs), which can work as reactive processing aids to replace conventional plasticizers and are used as prepolymers to synthesize novel block copolymers. However, the understanding of effects of their microstructures on the properties of materials is still not sufficient. In this study, liquid 1,4-polyisoprene (L1,4-IR) and liquid 3,4-polyisoprene (L3,4-IR) with similar molecular weight were selected and mixed with styrene-butadiene rubber (SBR)/butadiene rubber (BR). The effects of microstructures of the LRs on the properties of materials were investigated. L1,4-IR has more 1,4-units and fewer 3,4-units than L3,4-IR. This gives L1,4-IR a lower glass transition temperature and much more flexible polymer chains. Vulcanizates containing L1,4-IR had advantages over samples containing L3,4-IR, including lower Mooney viscosities, smaller delta G' value from 0.3% to 43% of strain, fewer sol fractions, better abrasion resistance and lower values of tan delta at 60 ?. In contrast, high contents of 3,4-units endow L3,4-IR with low unsaturation in polymer backbones and high glass transition temperature. Samples containing L3,4-IR showed higher values of tan delta at 0?, better thermal stabilities and excellent DIN abrasion resistance after aging compared to samples with L1,4-IR. Furthermore, there were no big differences in the mechanical properties of SBR/BR compounds containing L1,4-IR or L3,4-IR. The results of this study are of great importance to the practical application of liquid polyisoprene in the rubber industry. (c) 2023 Society of Industrial Chemistry.
卷号:72
期号:9
是否译文:

张春雨

教授 博士生导师 硕士生导师

教师拼音名称:zhangchunyu

出生日期:1978-11-30

电子邮箱:

入职时间:2019-11-28

所在单位:先进橡胶材料教育部重点实验室

学历:博士研究生

办公地点:国家大学科技园北楼702 CCF大楼1517室

性别:男

联系方式:13844852208

学位:理学博士

毕业院校:吉林大学

所属院系:先进橡胶材料教育部重点实验室

学科:材料科学与工程其他专业
高分子化学与物理

崂山校区 - 山东省青岛市松岭路99号   
四方校区 - 山东省青岛市郑州路53号   
中德国际合作区(中德校区) - 山东省青岛市西海岸新区团结路3698号
高密校区 - 山东省高密市杏坛西街1号   
济南校区 - 山东省济南市文化东路80号©2015 青岛科技大学    
管理员邮箱:master@qust.edu.cn
访问量: 手机版 English 青岛科技大学

最后更新时间: ..