Synthesis and characterization of bifuntional magnetic-optical Fe<inf>3</inf>O<inf>4</inf>@Hollow@ZnS core-shell microspheres

发布时间:2023-10-19点击次数:

  • 关键字:Sulfur compounds;Energy transfer - Fluorescence - Fluorescence quenching - II-VI semiconductors - Iron oxides - Microspheres - Photocatalysis - Quenching - Silica - Zinc sulfide;Blue light emissions - Core-shell microspheres - Core/shell - Fluorescence spectrophotometer - Hollow structure - Magnetic-optical - Photocatalytic property - Synthesis and characterizations
  • 摘要:Bifunctional Fe<inf>3</inf>O<inf>4</inf>@ZnS microspheres with hollow heterostructures have been successfully fabricated by a simple hard-templating method. XRD, TEM, MPMS, and fluorescence spectrophotometer had been to investigate the as-prepared materials. The results showed that there is controllable hollow structure between Fe<inf>3</inf>O<inf>4</inf>cores and ZnS layer. The Ms values of Fe<inf>3</inf>O<inf>4</inf>and Fe<inf>3</inf>O<inf>4</inf>@Hollow@ZnS microspheres are 86.2 emu/g and 53.1 emu/g at 300 K, respectively. When excited by 353 nm low-power UV lamps, the composites have a broad blue light emission band between 440 and 500 nm. As the hard template, the amorphous SiO<inf>2</inf>plays a key role in the forming process of the hollow structure. The presence of the hollow structures blocks the energy transfer between ZnS and Fe<inf>3</inf>O<inf>4</inf>particles, which reduces the probability of fluorescence quenching. Furthermore, the hollow cavity size of the microspheres can be easily controlled by adjusting the thickness of SiO<inf>2</inf>layer, which can affect the photocatalytic properties.<br/> &copy; 2018 Elsevier B.V.
  • 卷号:212
  • 期号:
  • 是否译文:否
+
论文成果

个人信息

  • 职称:教授
  • 学历:博士研究生
  • 学位:博士
  • 职务:科技处副处长
  • 电子邮箱:

其他联系方式

  • 移动电话:
  • 邮箱: