Controllable formation of amorphous structure to improve the oxygen evolution reaction performance of a CoNi LDH

发布时间：2023-10-19点击次数：

关键字：LAYERED DOUBLE HYDROXIDE; HIGHLY EFFICIENT; NANOSHEETS; COBALT; ELECTROCATALYST; IRON
摘要：The morphology design of layered double hydroxides (LDHs) is an important way to determine the catalytic performance of LDH materials. A novel structure of CoNi LDH sheets with amorphous structure on the edge was prepared by electrooxidation. It was characterized by XRD, SEM, TEM and XPS. It was found that during the electrooxidation, some of the Co2 ions were oxidized to Co3 to form amorphous CoOOH intermediates, which promoted the OER performance. The electrochemical test results show that CoNi LDH treated by electrooxidation for 6 hours has an ultra-low overpotential of 206 mV at a current density of 10 mA cm(-2), and can work stably under alkaline conditions for more than 10 hours. This work suggests that introducing an amorphous structure on LDH through electrooxidation produces abundant active sites, which is an easy and efficient method to improve the OER performance of CoNi LDHs.
卷号：13
期号：4
是否译文：否

论文成果

个人信息