Synthesis and characterization of bifuntional magnetic-optical Fe3O4@Hollow@ZnS core-shell microspheres

发布时间:2023-10-19点击次数:

  • 关键字:Core/shell, Magnetic-optical, Photocatalytic properties
  • 摘要:Bifunctional Fe3O4@ZnS microspheres with hollow heterostructures have been successfully fabricated by a simple hard-templating method. XRD, TEM, MPMS, and fluorescence spectrophotometer had been to investigate the as-prepared materials. The results showed that there is controllable hollow structure between Fe3O4 cores and ZnS layer. The Ms values of Fe3O4 and Fe3O4@Hollow@ZnS microspheres are 86.2 emu/g and 53.1 emu/g at 300 K, respectively. When excited by 353 nm low-power UV lamps, the composites have a broad blue light emission band between 440 and 500 nm. As the hard template, the amorphous SiO2 plays a key role in the forming process of the hollow structure. The presence of the hollow structures blocks the energy transfer between ZnS and Fe3O4 particles, which reduces the probability of fluorescence quenching. Furthermore, the hollow cavity size of the microspheres can be easily controlled by adjusting the thickness of SiO2 layer, which can affect the photocatalytic properties.
  • 卷号:
  • 期号:212
  • 是否译文:否
+
论文成果

个人信息

  • 职称:教授
  • 学历:博士研究生
  • 学位:博士
  • 职务:科技处副处长
  • 电子邮箱:

其他联系方式

  • 移动电话:
  • 邮箱: