Application of SiO2 spheres in the synthesis of coiled carbon nanofibers with high purity

关键字:LARGE-SCALE SYNTHESIS; ELECTRICAL-CONDUCTIVITY; NANOTUBE FIBERS; CVD SYNTHESIS; TEMPERATURE; NANOSTRUCTURES; NANOMATERIALS; MORPHOLOGY

摘要:During a chemical vapor deposition synthesis process of carbon fibers, copper-based catalyst particles tend to aggregate into larger secondary particles and lead to the growth of straight carbon fibers with large diameters. The introduction of silicon dioxide spheres can provide enough sites to uniformly disperse catalyst particles and prevent the agglomeration of adjacent catalyst particles, and thereby coiled carbon nanofibers are synthesized using common copper-based salts without special pretreatment, including copper chloride, copper nitrate and copper sulfate. The size of copper-based catalyst particles is about 10 to 15 nm. Also, effects of the concentration of copper-based salt catalyst and reaction temperature on coiled carbon fibers are investigated. Furthermore, silicon dioxide spheres can be removed easily by NaOH solution to obtain coiled carbon nanofibers.

卷号:102

期号:wu

是否译文:

崂山校区 - 山东省青岛市松岭路99号   
四方校区 - 山东省青岛市郑州路53号   
中德国际合作区(中德校区) - 山东省青岛市西海岸新区团结路3698号
高密校区 - 山东省高密市杏坛西街1号   
济南校区 - 山东省济南市文化东路80号©2015 青岛科技大学    
管理员邮箱:master@qust.edu.cn