Preparation of highly efficient high-entropy alloy catalysts with electrodeposition and corrosion engineering for OER electrocatalysis

发布时间:2024-12-23  点击次数:

关键字:OXYGEN EVOLUTION; FILM

摘要:High entropy alloy (HEA) has recently gained attention as one of the promising materials for catalytic field because of its unique structure and multi-constituent synergy catalytic applications due to its diverse element composition and multi-constituent synergy that offered excellent thermal stability, catalytic activity and corrosion resistance. In the work, we introduce the facile preparation of a self-supporting HEA-FeMnCuCo via one-step electrodeposition method, followed by generating HEA multicomponent hydroxyl oxide via a corrosion engineering approach to acquire an efficient and stable alkaline electrolytic catalyst. The prepared catalyst exhibits a remarkable catalytic performance with the overpotentials of 226 mV at current densities of 10 mA cm(-2), and a low Tafel slope of 58.2 mV.dec(-1). And the high activity is attributed to the formation of transition metal elements (Ni/Fe/Co) with high oxidation states by a corrosion engineering, which increase the active sites and reduced the initial potential of oxygen evolution reaction. Additionally, the HEA catalyst exhibits an excellent long-term OER stability, lasting over 100 h at 50 mA cm(-2).

卷号:57

期号:

是否译文:

崂山校区 - 山东省青岛市松岭路99号   
四方校区 - 山东省青岛市郑州路53号   
中德国际合作区(中德校区) - 山东省青岛市西海岸新区团结路3698号
高密校区 - 山东省高密市杏坛西街1号   
济南校区 - 山东省济南市文化东路80号©2015 青岛科技大学    
管理员邮箱:master@qust.edu.cn

访问量:| 最后更新时间:--| 开通时间:-- |手机版