Effect of pulse duty cycle on micro-plasma oxidation of aluminum alloy

发布时间:2021-03-15  点击次数:

关键字:pulse duty cycle; micro-plasma oxidation; oxide coatings; aluminum alloy

摘要:The pulse power supply was applied to oxidation of an aluminum alloy by means of micro-plasma discharge in electrolyte solutions. The LY12 aluminum alloy was used as specimen in the form of a disc 20 mm in diameter and 6 mm in thickness. The electrolyte solutions consist of a sodium silicate or phosphate, etc., with pH value in the range of 7-12. The working voltage was 120-600 V. The current density was 10-60 A/dm(2) and the temperature of the electrolyte solution ranged from 10 degrees C to 60 degrees C during oxidation. The properties of oxidation coating were characterized by surface and structural analytical techniques, i.e., scanning electron microscopy and X-ray diffraction analysis. It was ascertained that the thickness of the coating can be from a few micrometers up to more than 200 pm with a good adhesion between the coating and the substrate, and the coatings comprised a mixture of crystallized delta-Al2O3, gamma-Al2O3, and alpha-Al2O3. The hardness of the coating was measured using a Vickers hardness tester with a 50 g load. The mean value of microhardness was HV 1200-2200 kgf/mm(2). (C) 2005 Elsevier B.V, All rights reserved.

卷号:59

期号:22

是否译文:

崂山校区 - 山东省青岛市松岭路99号   
四方校区 - 山东省青岛市郑州路53号   
中德国际合作区(中德校区) - 山东省青岛市西海岸新区团结路3698号
高密校区 - 山东省高密市杏坛西街1号   
济南校区 - 山东省济南市文化东路80号©2015 青岛科技大学    
管理员邮箱:master@qust.edu.cn

访问量:| 最后更新时间:--| 开通时间:-- |手机版