摘要：The styrene (ST)-2-methylhexyl acrylate (EHA) copolymer latexes were synthesized through two-stage seeded emulsion polymerization (TSSEP) technique which were compared with the conventional emulsion polymerization (CEP) technique. The morphologies, particle size and electrokinetic behaviors of TSSEP and CEP latexes were studied through transmission electron microscopy (TEM) and Zetasizer respectively. It was found that the latex particles of TSSEP were all uniform and almost spherical in morphology. The particle size as well as polydispersity of TSSEP latex was smaller than that of CEP latex, and the particle size measurement of TEM corresponded with that of Zetasizer. Electrokinetic studies showed that all latexes were negative systems, and the particles exhibited colloidal stability under basic conditions. The negative value of zeta-potential for TSSEP latex was larger than that for CEP latex over the whole range of measured pH and NaCl concentrations, i.e. TSSEP latex demonstrated higher electrostatic stability than CEP latex. The zeta-potential reached the maximum value at approximately 3 x 10(-3) mol dm(-3) of NaCl concentration indicating the highest colloidal stability of TSSEP and CEP latexes. At very high salt concentration ([NaCl] = 0.1 M), we obtained very small zeta-potential values, thus the colloidal stability of ST-EHA copolymer latexes was much low.
卷号：82
期号：1
是否译文：否
上一条：炭黑与一维填料协同补强氟橡胶
下一条：分散剂对炭黑在NR中分散性的影响