Effects of plasticizing time on flexural fatigue of soft Poly(vinyl chloride)

关键字:MECHANICAL-PROPERTIES; PVC; PLASTISOLS; MORPHOLOGY; ELASTOMER; SOLVENT; POLYMER

摘要:In this study, seven gradient plasticizing time at 200 degrees C were set to explore the effects on Bally Flex fatigue of soft poly(vinyl chloride) (PVC). The results showed that the rotational rheometer was well used to characterize the plasticizing process of PVC paste. The optimum plasticizing temperature of soft PVC was about 180 degrees C. Within a certain range of plasticizing time, the glass transition temperature of soft PVC decreased with the extension of plasticizing time, and the Bally Flex fatigue life was prolonged as the plasticizing time extended. When the plasticizing time was 105 s, the plasticization was nearly completed, which can be used as an optimum plasticizing time in terms of manufacturing efficiency and quality. When the plasticization time was 135 s, the degree of plasticization was the highest. The fatigue cycles of Bally Flex and breaking energy (W) at -20 degrees C were 136,000 and 4850 J center dot m(-3), respectively. It was concluded that Bally Flex fatigue life and W had a good positive correlation. Thus, the tensile test can be used as a simple approach to predict the Bally Flex fatigue life trend of soft PVC specimens.

卷号:55

期号:2

是否译文:

崂山校区 - 山东省青岛市松岭路99号   
四方校区 - 山东省青岛市郑州路53号   
中德国际合作区(中德校区) - 山东省青岛市西海岸新区团结路3698号
高密校区 - 山东省高密市杏坛西街1号   
济南校区 - 山东省济南市文化东路80号©2015 青岛科技大学    
管理员邮箱:master@qust.edu.cn