Research on interfacial microstructure of Ti-coated diamond brazed and uncoated diamond brazed by high-frequency induction

关键字:Ti-coated diamond; uncoated diamond; high-frequency induction brazing; interfacial microstructure; bond strength

摘要:The Ti-coated diamond and the uncoated diamond were brazed with Ni-based filler alloy by high-frequency induction under argon atmosphere at 1050 degrees C within 15 seconds. The interfacial microstructures between brazed diamond and the filler alloy were analyzed by scanning electron microscopy (SEM), energy dispersion spectrometer (EDS) and X-ray diffraction (XRD). It is surprisedly found that Cr-carbides forms normally and compactly on the surface of Ti-coated diamond brazed, whereas Cr-carbide forms tangentially and loosely on, the surface of uncoated diamond brazed. The abrade experiment results for the brazed diamonds show that the bond strength between the normally formed Cr-carbide and the diamond is higher than that between Cr-carbide and uncoated diamond brazed. Furthermore, the cause that Ti changes the morphology of Cr-carbides on the surface of Ti-coated diamond brazed is discussed by the further tests specially designed.

卷号:359-360

期号:

是否译文:

崂山校区 - 山东省青岛市松岭路99号   
四方校区 - 山东省青岛市郑州路53号   
中德国际合作区(中德校区) - 山东省青岛市西海岸新区团结路3698号
高密校区 - 山东省高密市杏坛西街1号   
济南校区 - 山东省济南市文化东路80号©2015 青岛科技大学    
管理员邮箱:master@qust.edu.cn