Compositing fluid infused in superhydrophobic Cu(OH)(2) nanoneedle matrix to inhibit abiotic and microbiologically induced corrosion of Cu in seawater environment

关键字:SUPER-HYDROPHOBIC FILM; CARBON-FIBER; SURFACE; FABRICATION; COPPER; SELF; BARRIER; PROTECTION; COATINGS; ZINC

摘要:Although superhydrophobicity (SHP) and liquid infused surface (LIS) bio-inspired by the lotus leaf and pitcher plant have afforded high corrosion inhibition to metals, they still have the drawbacks such as short term duration and drainage in water phase. In this report, using a facile electrochemical anodization approach, Cu(OH)(2) nanoneedle matrix is built onto Cu substrate. The surface modification with dodecanethiol enables superhydrophobicity wettability. Oil and hydrophobic ZnO nanoparticle obtained by modification with dodecanethiol realize compositing liquid infused surface (CLIS) on Cu surface. For superhydrophobic Cu(OH)(2) layer, its corrosion inhibition to Cu is limited. However, when Cu metal is covered with compositing fluid, the corrosion inhibition capability to abiotic and biotic corrosion induced by sulfate reducing bacteria has been remarkably enhanced. After immersion in seawater for 20 days, Z(0.01Hz) of CLIS Cu is still as high as 1.30 x 10(9) Omega.cm(2), confirming the higher protection efficiency than SHP and LIS coverage. For biotic corrosion inhibition, after soaking for 10 days in sulfate reducing bacteria suspension, Z(0.01 Hz) of CLIS Cu still remains 1.25 x 10(5) Omega.cm(2), which is much higher than SHP Cu and LIS Cu. Hydrophobic nanoparticles work as the additional absorption matrix to further anchor oil phase, so that drainage will be avoided. The duration of the coating is enhanced. Therefore, CLIS layer has afforded a versatile route to protect Cu from both seawater corrosion and microbiologically induced corrosion.

卷号:142

是否译文:

崂山校区 - 山东省青岛市松岭路99号   
四方校区 - 山东省青岛市郑州路53号   
中德国际合作区(中德校区) - 山东省青岛市西海岸新区团结路3698号
高密校区 - 山东省高密市杏坛西街1号   
济南校区 - 山东省济南市文化东路80号©2015 青岛科技大学    
管理员邮箱:master@qust.edu.cn