关键字：Diamond; Brazing; High-frequency induction; Interfacial microstructure; Bond strength

摘要：The high-powered brazing diamond saw was developed to cut vehicle tyre efficiently. The Ti-coated diamond and the uncoated diamond were brazed with NiCr alloy by high-frequency induction under argon atmosphere at 1020 degrees C within 10 seconds. The interfacial microstructures between brazed diamond and the filler alloy were analyzed by scanning electron microscopy (SEM), X-ray diffraction (XRD) and energy dispersion spectrometer (EDS). It is surprisedly found that Cr-carbides forms compactly and normally on the surface of Ti-coated diamond brazed, whereas Cr-carbide forms loosely and tangentially on the surface of uncoated diamond brazed. The abrade experiment results for the brazed diamonds show that the bond strength between the Cr-carbide and uncoated diamond brazed is lower than the normally formed Cr-carbide and the diamond. Furthermore, the cause that Ti changes the morphology of Cr-carbides on the surface of Ti-coated diamond brazed is discussed by the further tests that are specially designed.

卷号：87-88

是否译文：否