Synthesis of CF@PANI hybrid nanocomposites decorated with Fe3O4 nanoparticles towards excellent lightweight microwave absorber
- 发布时间：2023-10-19
- 点击次数：
- 关键字：CF@PANI@Fe3O4 nanocomposites; Microwave absorber; Lightweight; Low filler content; Attenuation mechanism
- 摘要：Recently, lightweight has gradually become the most concerned property for a practical microwave absorber in the frequency range of 2-18 GHz. In this work, using commercial carbon fiber (CF) as matrix, the hybrid nanocomposites constructed by CF core, polyaniline (PANI) coating and dispersed Fe3O4 nanoparticles (NPs) were successfully synthesized by the electrodeposition and subsequent hydrothermal process. The systematic characterization results revealed that both PANI and Fe3O4 exerted positive roles in enhancing the microwave absorption properties of bare CF. Under the combined action of various components, the desired products (CF@PANI@Fe3O4 hybrid nanocomposites) exhibited remarkable microwave absorption performances, and the minimal reflection loss (RL) was -46.86 dB at a filler content of 10 wt% and a matching thickness of 2.7 mm. Moreover, a synergistic mechanism was proposed according to multiple reflection/scattering, dipole polarization, interface polarization, eddy current and magnetic resonance, so as to demonstrate the multi-attenuation approaches of the incident electromagnetic wave. (C) 2020 Elsevier Ltd. All rights reserved.
- 卷号：174
- 期号：No
- 是否译文：否
- 上一条：Designable synthesis of reduced graphene oxide modified using CoFe2O4 nanospheres with tunable enhanced microwave absorption performances between the whole X and Ku bands
- 下一条：Synergy Strategy of Electrical Conductivity Enhancement and Vacancy Introduction for Improving the Performance of VS4 Magnesium-Ion Battery Cathode