One-step synthesis of flower-like Bi2O3/Bi2Se3 nanoarchitectures and NiCoSe2/Ni0.85Se nanoparticles with appealing rate capability for the construction of high-energy and long-cycle-life asymmetric aqueous batteries

  • 发布时间:2023-10-19
  • 点击次数:

  • 关键字:Bismuth compounds;Electrochemical electrodes - Nanoparticles - Nickel compounds - Secondary batteries - Selenium compounds - Synthesis (chemical)
  • 摘要:The intelligent construction of electrode nanostructures with unique morphologies is of admirable importance for increasing the energy storage capacity of highly efficient supercapacitor devices. In this study, the negative electrode material Bi<inf>2</inf>O<inf>3</inf>/Bi<inf>2</inf>Se<inf>3</inf> nanoflower (Bi<inf>2</inf>O<inf>3</inf>/Bi<inf>2</inf>Se<inf>3</inf> NFs) hybrid was first fabricated via a simple one-step solvothermal approach; due to the favorable conductivity of Bi<inf>2</inf>Se<inf>3</inf>, high theoretical capacity of Bi<inf>2</inf>O<inf>3</inf> and their distinctive nanostructures, the achieved Bi<inf>2</inf>O<inf>3</inf>/Bi<inf>2</inf>Se<inf>3</inf> NFs exhibited the maximum specific capacity of 132.7 mA h g<sup>-1</sup> (∼531 F g<sup>-1</sup>) at 1 A g<sup>-1</sup> and the superior rate capability of 113.8 mA h g<sup>-1</sup> (∼455 F g<sup>-1</sup>) at 10 A g<sup>-1</sup>. Moreover, the positive electrode material NiCoSe<inf>2</inf>/Ni<inf>0.85</inf>Se nanoparticles (NiCoSe<inf>2</inf>/Ni<inf>0.85</inf>Se NPs) obtained by an electrodeposition method delivered the high specific capacity of 248.4 mA h g<sup>-1</sup> (∼1788 F g<sup>-1</sup>) at 1 A g<sup>-1</sup> as well as the appealing rate property of ∼84% capacity retention when the current density was increased by 100 times (i.e., 100 A g<sup>-1</sup>). More significantly, it was found that the assembled Bi<inf>2</inf>O<inf>3</inf>/Bi<inf>2</inf>Se<inf>3</inf> NFs//NiCoSe<inf>2</inf>/Ni<inf>0.85</inf>Se NP asymmetric aqueous battery (AAB) device achieved the extraordinary energy density of 88.4 W h kg<sup>-1</sup> at the power density of 2.4 kW kg<sup>-1</sup> along with a durable lifespan (maintaining the capacity retention of up to 91.5% even after 10000 cycles). Consequently, the design strategy and novel perspectives reported herein not only hold extensive promise for expanding the preparation techniques of morphology-controlled composites with robust electrochemical properties but also promote the practical applications of newly emerging metal selenides in next-generation aqueous batteries.<br/> © The Royal Society of Chemistry 2019.
  • 卷号:7
  • 期号:29
  • 是否译文:

崂山校区 - 山东省青岛市松岭路99号   
四方校区 - 山东省青岛市郑州路53号   
中德国际合作区(中德校区) - 山东省青岛市西海岸新区团结路3698号
高密校区 - 山东省高密市杏坛西街1号   
济南校区 - 山东省济南市文化东路80号©2015 青岛科技大学    
管理员邮箱:master@qust.edu.cn