Synthesis of N-doped multi-cavity Sn/C composite and utilization to anode in lithium ion batteries
- 发布时间：2021-06-29
- 点击次数：
- 摘要：Sn based materials have drawn significant research interests owning to their excellent performances as anodes in lithium ion batteries (LIBs). However, the enormous volume change, together with severe Sn particles aggregation during repeated redox cycles present major obstacles for the commercial application in LIBs. Here a simple and scalable approach is developed to construct the nitrogen-doped multi-cavity Sn/C composite through introduction of the polymeric g-C3N4 material which acts as supporting base to anchor 4-6 nm ultrafine active nanoparticles in mild conditions and further as sacrificial agent to produce voids as well as nitrogen dopant for the carbon shell during high temperature pyrolysis. As a result, the nitrogen-doped multi-cavity Sn/C anode displays high specific capacity of 512 mA h g(-1) at 1.0 A g(-1), good capacity retention of 82% after 1000 cycles and excellent rate performance when used as anode for LIBs.
- 卷号：260
- 是否译文：否