Facile synthesis of CeTa4þ co-doped NaTaO3 and rGO nanocomposites with enhanced visible light photocatalytic performance

关键字:HETEROJUNCTION PHOTOCATALYST; WATER; FABRICATION; REDUCTION; NANOCUBES; SEPARATION; COMPOSITE

摘要:Nanocomposites of C-Ta4 co-doped NaTaO3 and reduced graphene oxide (C-NTO/rGO) with highly efficient photocatalytic activity were fabricated by a one-step solvothermal reaction. The optimum composites C-NTO/3rGO (with 3 wt% rGO) exhibited superior photocatalytic activity for the degradation of RhB over a mono-component counterpart under visible light irradiation. The photocatalytic efficiency was found to be as high as 97% for 90 min. Both XRD and XPS characterizations indicated that the doping of carbon into the NaTaO3 lattice leads to the reduction of Ta5 to Ta4 . Furthermore, the co-doping significantly narrows the band gap (about 2.8 eV). Photo-luminescence (PL), time resolved transient PL decay spectra and photo-current results confirmed that photo-induced hole electron pairs can be effectively separated resulting from the introduction of rGO. The synergistic effect of a decreased band gap and highly effective separation of photo generated electrons and holes may be responsible for the enhanced photocatalytic activity of the fabricated nanocomposites. Both h and & BULL;OH active radicals were found to be the key factors for the photo-decomposition process of RhB over the nanocomposites, while , O-2(-) was also involved to a smaller extent. A possible photo-degradation mechanism for C-NTO/rGO was proposed on the basis of the experiments results. (c) 2022 Published by Elsevier Ltd on behalf of Hydrogen Energy Publications LLC.

卷号:47

期号:21

是否译文:

崂山校区 - 山东省青岛市松岭路99号   
四方校区 - 山东省青岛市郑州路53号   
中德国际合作区(中德校区) - 山东省青岛市西海岸新区团结路3698号
高密校区 - 山东省高密市杏坛西街1号   
济南校区 - 山东省济南市文化东路80号©2015 青岛科技大学    
管理员邮箱:master@qust.edu.cn