关键字：ZSM-5 Nanoparticles; Porous materials; Al-SBA-15; Monolith

摘要：The amorphous wall structure of Al-SBA-15 was converted in-situ to uniform ZMS-5 nanocrystal aggregates. Si/Al ratio in resulting ZSM-5 nanocrystal aggregates is close to that of raw Al-SBA-15. The ZSM-5 aggregates exhibits a monolithic morphology, a replica of the shape of raw Al-SBA-15, which significantly allows the avoidance of a high-speed centrifugal separation process. The incompletely decomposed structure-directing template of Al-SBA-15 works as inert units inserting in the mesopores of Al-SBA-15 materials. The nucleation and growth of zeolite were physically confined inside a nano-scale space surrounded by the chemically inert units that were generated from the controlled decomposition of the surfactant.