Strategically Designed Zeolitic Imidazolate Frameworks for Controlling the Degree of Graphitization

关键字:METAL-ORGANIC FRAMEWORK; DE-NOVO APPROACH; NANOPOROUS CARBONS; HYDROGEN STORAGE; COORDINATION POLYMER; DIRECT CARBONIZATION; EMBEDDING ENZYMES; POROUS CARBON; NANOARCHITECTURES; SUPERCAPACITORS

摘要:The zeolitic imidazolate frameworks (ZIFs) ZIF-8 and ZIF-67 are well-known as belonging to the series of metal-organic frameworks. Using different types of metal ions in them, such as Zn2+ and Co2+ simultaneously, brings both advantages and disadvantages with respect to the carbonization process. For tailoring their properties, we suggest that the best approach involves control of the bimetallic ZIF-derived carbon nanoarchitecture, which is hybridized through the synergistic effects of each metal ion. In this study, the bimetallic ZIFs were designed by controlling the molar ratio of zinc (Zn2+) and cobalt (Co2+ ) ions, and the carbon nanoarchitecture was subsequently formed by a facile heat treatment and acid leaching. We demonstrate this approach to achieve tailored ZIF derived carbon nanoarchitectures with different pore sizes, surface areas, and degree of graphitization. These pave the way to finding the optimal carbon nanoarchitecture for specific applications such as Li-O-2 air cell.

卷号:91

期号:10

是否译文:

崂山校区 - 山东省青岛市松岭路99号   
四方校区 - 山东省青岛市郑州路53号   
中德国际合作区(中德校区) - 山东省青岛市西海岸新区团结路3698号
高密校区 - 山东省高密市杏坛西街1号   
济南校区 - 山东省济南市文化东路80号©2015 青岛科技大学    
管理员邮箱:master@qust.edu.cn