Nitrogen- and oxygen-containing hierarchical porous carbon frameworks for high-performance supercapacitors

发布时间:2024-01-19  点击次数:

关键字:Nitrogen functional groups; Oxygen functional groups; Porous carbon frameworks; Polyaniline; Supercapacitors

摘要:Nitrogen- and oxygen-containing hierarchical porous carbon frameworks have been successfully synthesized by carbonization and simultaneous activation of polyaniline with KOH as activating agent. The obtained porous carbon frameworks with hierarchical pore structures show high specific surface area (2280.0 m(2) g(-1)), large total pore volume (1.75 cm(3) g(-1)), and abundant nitrogen (5.7 at.%) and oxygen (14.4 at.%) functional groups. As expected, the porous carbon frameworks synthesized with a KOH/polyaniline weight ratio of 4:1 exhibit improved capacitance properties, such as an enlarged specific capacity (428.1 Fg(-1) at 0.5 Ag-1), excellent rate capability (299.7 Fg(-1) at 50 Ag-1), and excellent cycling stability. The specific power density and energy density can reach 14275 W kg(-1), and 18.6 Wh kg(-1), respectively. This method is facile, low cost, and effective for the production of nitrogen- and oxygen-containing carbon materials with high specific surface area, which can be applied in high-performance supercapacitors. (C) 2014 Elsevier Ltd. All rights reserved.

卷号:134

期号:

是否译文:

崂山校区 - 山东省青岛市松岭路99号   
四方校区 - 山东省青岛市郑州路53号   
中德国际合作区(中德校区) - 山东省青岛市西海岸新区团结路3698号
高密校区 - 山东省高密市杏坛西街1号   
济南校区 - 山东省济南市文化东路80号©2015 青岛科技大学    
管理员邮箱:master@qust.edu.cn

访问量: | 最后更新时间:-- | 开通时间:-- |手机版