Gradient-tailored and heterointerface-rich architectures enable superior Li-ion storage performances of GeS2@NiS@N-doped carbon microspheres

发布时间:2024-01-19  点击次数:

关键字:ANODE MATERIAL; RECENT PROGRESS; LITHIUM; NIS; NANOSHEETS; EVOLUTION; GES2

摘要:The mesoporous compositional gradient nitrogen-doped carbon encapsulated germanium disulfide-nickel sulfide (abbreviated as "GeS2@NiS@N-C ") microspheres have been synthesized. The Ni3Ge2O5(OH)(4) microspheres precursor is firstly prepared by a hydrothermal mineralization process, which transforms to Ge3Ni5 microspheres by high temperature reduction. A thin polydopamine shell protects the microsphere architecture, which is converted into nitrogen-doped carbon layers. The GeS2@NiS@N-C microspheres are finally fabricated via a high temperature interdiffusion vulcanization process induced by Kirkendall effect, during which the interdiffusion rate of Ni atoms is much faster than that of Ge atoms leading to the gradual composition changes from the exterior (NiS phase is rich) to the interior (GeS2 phase is rich) throughout a single microsphere. The GeS2@NiS@N-C microspheres show unique structural advantage of the abundant heterogeneous interfaces, which accelerates the Li+ diffusion kinetics proved by density functional theory results. Besides, the in-situ XRD analyses reveal a continuous lithiation sequence as the compositional gradient from NiS to GeS2, during which the in-situ generated Ni clusters from NiS construct a continuous and penetrating e(-) transport channel throughout the microsphere. As a result, the GeS2@NiS@N-C microspheres exhibit improved cycling stability and rate capability when employed as anodes for lithium ion batteries.

卷号:605

期号:

是否译文:

崂山校区 - 山东省青岛市松岭路99号   
四方校区 - 山东省青岛市郑州路53号   
中德国际合作区(中德校区) - 山东省青岛市西海岸新区团结路3698号
高密校区 - 山东省高密市杏坛西街1号   
济南校区 - 山东省济南市文化东路80号©2015 青岛科技大学    
管理员邮箱:master@qust.edu.cn

访问量: | 最后更新时间:-- | 开通时间:-- |手机版