Synthesis and electrochemical performance of phosphate-coated porous LiNi1/3Co1/3Mn1/3O2 cathode material for lithium ion batteries

Release time:2021-03-15 Hits:

Key Words:LiNi1/3Co1/3Mn1/3O2; Phosphate; Surface modification; Lithium ion batteries

Abstract:Porous LiNi1/3Co1/3Mn1/3O2 microspheres were synthesized by a co-precipitation approach combined with high-temperature calcination. To improve the electrochemical performances, phosphate coating was formed on the surfaces of porous LiNi1/3Co1/3Mn1/3O2 microspheres by H3PO4 etching and subsequent annealing treatment. As anticipated, phosphate-coated LiNi1/3Co1/3Mn1/3O2 microspheres (2 mol.% H3PO4) delivered discharge capacity of 100. 1 mAhg(-1) at 5 degrees C, which was higher than that of pristine LiNi1/3Co1/3Mn1/3O2 microspheres (64.8 mAh g(-1)). The improvement of rate capability and cycle stability of LiNi1/3Co1/3Mn1/3O2 microspheres could be attributed to the phosphate coating, which suppressed the side reaction between cathode and electrolyte. The phosphate surface modification has a promising application in improving the performance of layered oxide cathode materials for lithium ion batteries. (C) 2013 Elsevier Ltd. All rights reserved.