An environment-friendly calcium phosphate conversion coating on AZ91D alloy and its corrosion resistance

Release time:2021-03-15 Hits:

Key Words:the coating was evaluated by potentiodynamic polarization test in 3.5wt% NaCl solution. Result

Abstract:An environment-friendly phosphate conversion coating free of chromate, fluorides, and nitrite was developed on AZ91D alloy through a facile chemical deposition method. The surface morphology and phase composition of the coating were characterized by field-emission scanning electron microscopy (FE-SEM) and X-ray diffraction (XRD). The corrosion resistance of the coating was evaluated by potentiodynamic polarization test in 3.5wt% NaCl solution. Results indicate that the calcium phosphate coating was composed of a large number of leaf-like and flower-like particles. The chemical composition of the conversion coating was CaHPO4 center dot 2H(2)O crystals. The coating can remarkably reduce the corrosion current density of the substrate. Introduction of triethanolamine (TEA) additive into the phosphating bath leads to denser coating and high anticorrosive property of the phosphate coating.

Volume:66

Issue:4

Translation or Not:no

Pre One:PANI-modified Pt/Na<inf>4</inf>Ge<inf>9</inf>O<inf>20</inf> with low Pt loadings: Efficient bifunctional electrocatalyst for oxygen reduction and hydrogen evolution

Next One:Three-dimensional Fe, N-doped carbon nanosheets on interconnected carbon skeletons as a highly efficient and stable electrocatalyst for oxygen reduction reaction