关键字：HYPERCROSSLINKED POROUS POLYMERS; CYCLIC CARBONATES; CATALYSTS; EPOXIDES; FIXATION; DIOXIDE; CAPTURE; MILD; HYDROXYL; OXIDE

摘要：Developing effective metal- and halogen-free heterogeneous catalysts for the CO2 cycloaddition remains a challenge. In this study, novel imidazole-based hyper-crosslinked polymers (HCP-BZ, HCP-BP and HCP-TBZ) with abundant N sites were constructed via a one-pot polymerization, and employed as heterogeneous catalysts for the CO2 cycloaddition reaction. The special skeletal pore structure with abundant hierarchical pore structures and uniformly distributed active sites were demonstrated by ious characterization technologies. The optimal HCPTBZ(16:1) exhibits a good CO2 selective adsorption performance with a CO2 adsorption capacity of 2.23 mmol/g and CO2/N2 adsorption selectivity of 41 at 273 K and 0.1 MPa. Additionally, the resulting catalyst HCP-TBZ (16:1) achieves an excellent catalytic performance with 96 % yield and 99 % selectivity without metal, halogen, cocatalyst and solvent additions (120 degrees C, 1.0 MPa CO2, 5 h). Moreover, the HCP-TBZ(16:1) also exhibits a satisfactory catalytic activity under the mild conditions (70 degrees C, 1.0 MPa CO2), and can effectively catalyze the cyclic carbonate preparation from the dilute CO2 (15 %CO2/85 %N2). The comparable catalytic activity and the determined structural stability, reusability and universality make the prepared imidazole-based HCPs a potential heterogeneous catalyst candidate for the CO2 cycloaddition. This study will provide some guidance for developing metal-free and halogen-free CO2 adsorption and conversion platforms.

卷号：348

期号：-

是否译文：否